| Brand | Zhongke Aobo |
|---|---|
| Origin | Beijing, China |
| Type | High-Purity Alumina (99% Al₂O₃) Ceramic Ball Mill Jar |
| Volume Range | 500–12,000 mL |
| Inner Diameter | 105–245 mm |
| Height | 200–300 mm |
| Wall Thickness | 7–10 mm |
| Bulk Density | ≥3.80 g/cm³ |
| Apparent Porosity | <1% |
| Flexural Strength | >350 MPa |
| Compressive Strength | >12,000 MPa |
| Dielectric Constant (1 MHz) | ~9.8 |
| Vickers Hardness (HV10) | ~1,600 |
| Chemical Composition | Al₂O₃ ≥99 wt%, R₂O ≤0.2 wt%, Fe₂O₃ ≤0.1 wt%, SiO₂ ≤0.2 wt% |
| Feed Size | ≤1,000 µm |
| Final Particle Size | ≥100 µm (typical output after standard milling cycles) |
| Batch Capacity | 1–10 kg (material-dependent, based on jar fill ratio and media loading) |
| Brand | Zhongke Aobo |
|---|---|
| Origin | Beijing, China |
| Model | Φ12–300 mm |
| Material Composition | ≥99% Al₂O₃, ≤0.2% R₂O, ≤0.1% Fe₂O₃, ≤0.2% SiO₂ |
| Bulk Density | ≥3.80 g/cm³ |
| Apparent Porosity | <1% |
| Flexural Strength | >350 MPa |
| Compressive Strength | >12,000 MPa |
| Dielectric Constant (1 MHz) | ~9.8 |
| Hardness (HRA) | 88 |
| Max. Input Particle Size | 20 mm |
| Min. Output Particle Size | 0.5 mm |
| Batch Capacity | 100 mL |
| Sample Type | Hard, brittle, non-ferrous, high-purity materials |
| Compliance | Suitable for ISO/IEC 17025-accredited labs requiring inert, non-contaminating sample preparation |
| Brand | Zhongke Aobo |
|---|---|
| Origin | Beijing, China |
| Model | ∅100–∅300 mm |
| Material | 99% Al₂O₃ High-Purity Alumina Ceramic |
| Bulk Density | ≥3.80 g/cm³ |
| Apparent Porosity | <1% |
| Flexural Strength | >350 MPa |
| Compressive Strength | >12,000 MPa |
| Dielectric Constant (1 MHz) | ~9.8 |
| Vickers Hardness | ≥1,400 HV (equivalent to HRA 88) |
| Chemical Purity | Al₂O₃ ≥99.0 wt%, R₂O ≤0.2 wt%, Fe₂O₃ ≤0.1 wt%, SiO₂ ≤0.2 wt% |
| Brand | Zhongke Aobo |
|---|---|
| Origin | Beijing, China |
| Model | FW80 |
| Voltage | AC 220 V, 50 Hz |
| Power | 200 W |
| Speed | 10,000 rpm |
| Chamber Dimensions | Φ80 × 40 mm |
| Batch Capacity | 50–400 g |
| Feed Size | ≤1 mm |
| Output Particle Size | 40–200 mesh (≈74–420 µm) |
| Minimum Output Granularity | ≥0.5 mm |
| Net Weight | 2.5 kg |
| Gross Weight | 2.7 kg |
| Equipment Type | Benchtop Impact Crusher |
| Sample Type | Hard, brittle, dry materials |
| Brand | Zhongke Aobo |
|---|---|
| Origin | Beijing, China |
| Model | Φ300 / Φ250 / Φ200 / Φ150 / Φ120 mm |
| Material | ≥99% Al₂O₃ High-Purity Alumina Ceramic |
| Bulk Density | ≥3.80 g/cm³ |
| Apparent Porosity | <1% |
| Flexural Strength | >350 MPa |
| Compressive Strength | >12,000 MPa |
| Dielectric Constant (1 MHz) | ~9.8 |
| Vickers Hardness | ~1700 HV (equivalent to HRA 88) |
| Max Feed Size | 15 mm |
| Minimum Output Particle Size | ≥0.5 mm |
| Batch Capacity | 100 g |
| Sample Compatibility | Hard, brittle, non-fibrous inorganic materials (e.g., oxides, salts, pharmaceutical excipients, catalysts) |
| Compliance | ASTM C704, ISO 6474-1, GB/T 7917.1–1987 |